Products List
- Organic Pigment
- Pigment Red Series
- Pigment Yellow Series
- Pigment Orange Series
- Pigment Violet Series
- Pigment Blue Series
- Pigment Green Series
- Pigment Presscake
- Chrome Pigment
- Inorganic Pigment
- Iron Oxide Pigment
- Pigment Chips
- Flush Pigment
- Metal-Complex Solvent dyes
- Solvent Dyes
- Basic Dyes
- Ceramic Pigment
- Photoluminescent Pigment
- Enamel Pigment
- Fluorescent Pigment
- Chemicals for Radiation-Curable
- Resin
- Gum Rosin
- Rosin Resin
- Polyamide Resin
- Nitrates Cellulose
- Additive
- Rheological Additive
- Sodium Periodate
- Benzophenone Flake
- Chlorinated EVA
- Chlorinated Polypropylene
- Copolymer
- Pigment Violet 23
- Pigment Yellow 180
- Pigment Red 208
- Pigment Red 122
Add: No.8 Xiyuan Three Road, 3rd Floor, Building A, Hangzhou, P.R.China (310030)
Tel: 0086-571-88491745
Fax: 0086-571-88491746
E-mail: sales@union-pigment.com
shirley@union-pigment.com
Web:http://www.union-pigment.com/
Tel: 0086-571-88491745
Fax: 0086-571-88491746
E-mail: sales@union-pigment.com
shirley@union-pigment.com
Web:http://www.union-pigment.com/
Enamel Pigment
| Enamel Pigments | ||||
| Company Code | Color | Chemical Composition | Heat Resistance | Application |
| UNE-201 | Cadmium Yellow | Cd - S | 900 ℃ | more |
| UNE-202 | Cadmium Yellow | Cd - S | 900 ℃ | more |
| UNE-203 | Cadmium Yellow | Cd - S | 900 ℃ | more |
| UNE-205 | Cadmium Yellow | Cd - S | 900 ℃ | more |
| UNE-212 | Orange Yellow | xCds.(1-x)CdSe | 900 ℃ | more |
| UNE-801 | Creamy Yellow | Pb-Sb-Sn-Zn | 900 ℃ | more |
| UNE-104 | Orange Red | xCds.(1-x)CdSe | 900 ℃ | more |
| UNE-103 | Cadmium Red | xCds.(1-x)CdSe | 900 ℃ | more |
| UNE-102 | Cadmium Red | xCds.(1-x)CdSe | 900 ℃ | more |
| UNE-101 | Dar Cadmium Red | xCds.(1-x)CdSe | 900 ℃ | more |
| UNE-701 | Enamel Red | Cr-Sn-Si-Ca | 1250℃ | more |
| UNE-702 | Pink | Cr-Sn-Si-Ca | 1250℃ | more |
| UNE-421 | Royal Blue | Si-Co-Zr-Zn | 1280 ℃ | more |
| UNE-401 | Sky Blue | Al-Co-Zn-Cr | 1280 ℃ | more |
| UNE-411 | Cobalt Blue | Al-Co-Zn | 1280 ℃ | more |
| UNE-301 | Peacock Green | Al-Co-Cr-Zn | 1280 ℃ | more |
| UNE-311 | Green | Al-Co-Cr-Zn | 1280 ℃ | more |
| UNE-321 | Blue Green | Al-Co-Cr-Zn | 1300 ℃ | more |
| UNE-322 | Blue | Al-Co-Cr-Zn | 1300 ℃ | more |
| UNE-331 | Dark Green | Al-Co-Cr-Zn | 1300 ℃ | more |
| UNE-341 | Blackish Green | Cr-Al-Co-Zn | 1300 ℃ | more |
| UNE-351 | Cr Green | Cr2O3 | 1300 ℃ | more |
| UNE-361 | Jade Green | Cr-Al-Co-Zn-Cds | 1300 ℃ | more |
| UNE-371 | Apple Green | Pr-V-Zr-Si | 1300 ℃ | more |
| UNE-601 | Brown | Fe-Cr-Zn | 1300 ℃ | more |
| UNE-901 | Sb-Sn Grey | Sn-Sb | 1300 ℃ | more |
| UNE-501 | Black | Fe-Cr-Cu | 1300 ℃ | more |
| UNE-502 | Black | Fe-Cr-Cu | 1300 ℃ | more |
| UNE-511 | Co Black | Fe-Cr-Cu-Co-Mn | 1300 ℃ | more |
| UNE-514 | Co Black | Fe-Cr-Cu-Co-Mn | 1300 ℃ | more |
| Ground Coat and One-coat Enamel Frits | ||||
| Reference No. | Description | Expansion | Firing | Application |
| Coefficient (10-7) | Temperature (°C) | |||
| UNG-102 | High Temp.Nickel Ground Coat | 301.8 | 840-880 | more |
| UNG-103 | High Temp.Nickel Ground Coat | 286.5 | 860-890 | more |
| UNG-104 | High Temp.Nickel Ground Coat | 290.1 | 840-880 | more |
| UNG-105 | High Temp. Antimony Molybdenum White Ground Coat | 297.1 | 840-870 | more |
| UNG-111 | Medium Temp.Co-Ni Ground Coat | 313.7 | 800-840 | more |
| UNG-112 | Medium Temp.Co-Ni Ground Coat | 292.1 | 820-860 | more |
| UNG-118 | Medium Temp.Nickel Ground Coat | 309.1 | 800-840 | more |
| UNG-124 | Low Temp. Antimony Molybdenum White Ground Coat | 290.1 | 780-820 | more |
| UNG-1102 | High Temp.Co-Ni Ground Coat | 300.5 | 840-880 | more |
| UNG-1112 | Medium Temp.Co-Ni Ground Coat | 283.6 | 830-860 | more |
| UNG-1122 | Low temp.Co-Ni Ground coat | 300.5 | 780-820 | more |
| UNG-2400 | Low Temp.Co-Ni Ground Coat | 322.1 | 760-800 | more |
| UNG-2401 | Medium temp.Co-Ni Ground Coat | 292.1 | 800-840 | more |
| UNG-2404 | High Temp.Co-Ni Ground Coat | 290.1 | 840-870 | more |
| UNG-2405 | High Yemp.Co-Ni Ground Coat | 288.1 | 860-880 | more |
| UNG-2406 | Temp. Resistant Co-Ni Ground Coat | 278.2 | 860-900 | more |
| UNG-2414 | Low Temp. Co-Ni Ground Coat | 311.1 | 760-800 | more |
| UNG-2115 | One-coat Black Enamel | 296.1 | 830-850 | more |
| Remarks: directly coated on base metal.with strong adherence. wide range of firing temperature. | ||||
| 1. Mill Addition Ratio for Nickel and Co-Ni Ground Coat: | ||||
| Frit | 100 | Clay | 5-7 | |
| Quartz porwder | 0-8 | Borax | 0.3-0.5 | |
| Sodium Nitrite | 0.2-0.3 | Water | 50-55ml | |
| 2. Mill Addition Ratio of Sb-Mo Ground Coat: | ||||
| Frit | 100 | Antimony Oxide | 1.0 | |
| Clay | 5-7 | Barium Molybdate | 1.0 | |
| Quartz Powder | 0-8 | Water | 50-55 ml | |
| Frit Slurry Fineness | 1-2g/150mesh.100ml | Specific Gravity | 160-170g/100 ml | |
| Cover Coat Enamel Frits | ||||
| Reference No. | Description | Expansion | Firing | Application |
| Coefficient (10-7) | Temperature (°C) | |||
| UNC-202 | High Temp. Titanium White Enamel | 272.5 | 820-850 | more |
| UNC-203 | High Temp. Titanium White Enamel | 260.7 | 830-860 | more |
| UNC-211 | Medium Temp. Titanium White Enamel | 276.1 | 820-840 | more |
| UNC-222 | Low Temp. Titanium White Enamel | 280.7 | 780-820 | more |
| UNC-204 | High Temp.Titanium Cream Yellow Enamel | 283.5 | 820-860 | more |
| UNC-223 | Low Temp.Titanium Cream Yellow Enamel | 284.3 | 780-820 | more |
| UNC-213 | Titanium Ivory Enamel | 281.5 | 820-860 | more |
| UNC-214 | Medium Temp.Titanium Cream Yellow Enamel | 282.5 | 820-840 | more |
| UNC-206 | Titanium Laky Blue Enamel | 293.4 | 800-840 | more |
| UNC-208 | Titanium Apple Green Enamel | 292.5 | 800-840 | more |
| UNC-228 | Titanium Peachblow Enamel | 286.5 | 800-840 | more |
| UNC-218 | Antimony White Enamel | 327.2 | 820-860 | more |
| UNC-209 | Titanium Blue-gray Enamel | 276.1 | 800-840 | more |
| UNC-205 | Titanium Dark-gray Enamel | 257.1 | 800-840 | more |
| UNC-219 | Zirconium White Enamel | 259.5 | 820-860 | more |
| UNC-2200 | Super-white Enamel | 275.5 | 800-830 | more |
| Note: mainly Titanium and Antimony as opacifing agent.with good opacity and luster. as well as fine and smooth-clean surface.Colourful cover coat enamels possess bright luster. stable colour shade and good operation. When used. please note matching ground coat to select and firing temperature lower than ground coat. | ||||
| 1. Milling Addition Ratio of Titanium series frits: | ||||
| Frit | 100 | Clay | 5-6 | |
| Potassium Chlorate | 0-0.3 | Urea | 0-0.5 | |
| Water | 45-50ml | frit slurry fineness | 1-1.5g/160mesh.100ml | |
| specific gravity | 160-165g/100 ml | |||
| 2.Milling addition ratio of antimony series frits | ||||
| Frit | 100 | Clay | 6-7 | |
| water | 40-50ml | Frit slurry fineness | 1-2g/150mesh.100 ml | |
| Specific gravity | 170-175g/100ml | |||
| Transparent Enamel Frits | ||||
| Reference No. | Description | Expansion | Firing | Application |
| Coefficient (10-7) | Temperature (°C) | |||
| UNT-303 | High temp.semi-transparent enamel | 301.7 | 800-840 | more |
| UNT-315 | acid resistant transparent Enamel (Grade A) | 253.4 | 800-840 | more |
| UNT-316 | Mediumj temp.semi-transparent enamel | 300.4 | 800-840 | more |
| UNT-307 | Black enamel | 290.7 | 800-840 | more |
| UNT-309 | Royal Blue enamel | 302.2 | 800-840 | more |
| UNT-311 | Neutral white enamel 1# (opacity enamel) | 270.2 | 800-840 | more |
| UNT-1401 | transparent enamel | 286.1 | 800-840 | more |
| UNT-2305 | Acid resistant transparent enamel (Grade A ) | 284.3 | 820-840 | more |
| UNT-2306 | Acid resistant transparent enamel (Grade A) | 287.6 | 800-840 | more |
| Note: applied in colour decoration on surface of enamelware.with bright colour. stable colour shade.firing temperature lower than under enamel. | ||||
| 1. Mill addition ratio: | ||||
| frit | 100 | clay | 4-6 | |
| pigment | 2-6 | water | 45-50ml | |
| Note: adding proper pigment when ECF--307. ECF309 are used t o make colourful enamel frit . | ||||
| 2. Acid resistant transparent enamel milled 0.1~0.2 sodium aluminium | ||||
| frit fineness | spaying enamel | max 0.2g/200mesh.100 ml | ||
| enameling | 0.5-1g/ 150mesh.100 ml | |||
| Glass Enamel Frits | ||||
| Reference No. | Description | Expansion | Firing | Application |
| Coefficient (10-7) | Temperature (°C) | |||
| UNB-02 | glass blue enamel | - | 600-650 | more |
| UNB-03 | glass transparentenamel | - | 600-650 | more |
| UNB-04 | transparent glass enamel | - | 600-650 | more |
| UNB-05 | glass black enamel | - | 600-650 | more |
| UNB-06 | glass yellow-greenish | - | 600-650 | more |
| UNB-07 | glass semi- transparent enamel | - | 600-650 | more |
| UNB-08 | no-lead glass transparent enamel | - | 600-650 | more |
| Note: expansion coefficient and firing temperature conforming to glass. to make out various quality glass pigments through milling-adding some pigments. | ||||
| Aluminium-based Enamel Frits | ||||
| Reference No. | Description | Expansion | Firing | Application |
| Coefficient (10-7) | Temperature (°C) | |||
| UNA-01 | Aluminium-based Transparent Enamel | 382.3 | 530-550 | more |
| UNA-02 | Aluminium-based Transparent Enamel | 447.2 | 530-550 | more |
| UNA-03 | Aluminium-based No ¨Clead Transparent Enamel | 451.2 | 530-550 | more |
| UNA-04 | Aluminium-based No¨Clead Transparent Enamel | 433.6 | 530-550 | more |
| UNA-05 | Aluminium-based Titanium White Cover Coat | 449.4 | 530-550 | more |
| 1 Milling Addition Ratio: | ||||
| frit | 100 | Water Glass | 3-5 | |
| Borax | 3 | Acid Treatment | 2.5 | |
| Note: matching A-03 with A-04 commonly as per ratio 5:5, Mill-Adding to A-05 8% good quality titanium dioxide powder . | ||||
| Frit slurry fineness | passed on 250 mesh sieve | Specific Gravity | 180-190g/100 ml | |
| Cast-iron Enamel Frits | ||||
| Reference No. | Description | Expansion | Firing | Application |
| Coefficient (107) | Temperature (°C) | |||
| UNI-125 | cast iron black enamel | 334.2 | 760-780 | more |
| UNI-126 | cast iron black enamel | 332.4 | 760-780 | more |
| UNI-622 | thick cast iron black enamel | 314.4 | 750-780 | more |
| UNI-623 | thick cast-iron black enamel | 271.4 | 780-800 | more |
| UNI-625 | cast-iron black enamel | 244 | 760-780 | more |
| UNI-308 | cast-iron transparent enamel | 332.1 | 760-780 | more |
| UNI-1271 | thick cast iron black enamel | 274 | 750-780 | more |
| UNI-1308 | cast-iron transparent enamel | 283.1 | 760-780 | more |
| UNI-1309 | cast-iron transparent enamel | 335.5 | 740-760 | more |
| UNI-2700 | cast-iron opaque enamel | 289 | 780-800 | more |
| UNI-2707 | acid resistant cast iron black enamel | 305.6 | 780-800 | more |
| UNI-2708 | cast-iron white cover coat | 302.4 | 800-820 | more |
| UNI-2709 | acid resistant cast-iron white cover coat | 310.2 | 820-850 | more |
| Note: enameling on surface of cast iron, as called Wet-way Coating enamel first, cleaning the surface of earthen bowl after anneal . | ||||
| 1 Milling additon ratio for cast-iron black enamel: | ||||
| frit | 100 | clay | 5-7 | |
| quartz powder | 0-5 | borax | 0.5-0.8 | |
| sodium nitrite | 0.2 | black pigment | 2-5 | |
| water | 50-55 ml | |||
| note: adding 10-20% quartz powder in acid resistant black enamel | ||||
| frit slurry fineness | 0.5-1.0g/150mesh.100 ml | specific gravity | 160-170g/100ml | |
| 2 cast iron opaque enamel(sub-opaque enamel ) | ||||
| frit | 100 | clay | 5-6 | |
| borax | 0.5-0.8 | aluminium oxide | 2 | |
| water | 45-50ml | |||
| note: sub-opaque enamel consist of cast iron opaque enamel,with same milling addition ratio. | ||||
| frit slurry fineness | 1-1.5g/150¡¤100ml | specific gravity | 160-165g/100ml | |