Property |
Requirement |
|||
CR-501 |
CR-510 |
CR-513 |
CR-515 |
|
Mass Fraction of TiO2％≥ |
90 |
90 |
90 |
90 |
Color(In Conformity with Standard Sample)％≥ |
99 |
100 |
100 |
100 |
Oil Absorption g/100g≤ |
23 |
21 |
21 |
21 |
PH Value of Water Suspension |
7.0～9.5 |
6.5～8.5 |
7.0～8.5 |
7.0～8.5 |
Mass Fraction of Volatile Substance at 105℃ ％≤ |
0.8 |
0.8 |
0.8 |
0.8 |
Tint Reducing Power(Compared with Standard Sample )％≥ |
96 |
100 |
100 |
100 |
Screen Floating On 325 Mesh Sieve ％≤
|
0.05 |
0.05 |
0.05 |
0.05 |
Specific Resistance of Water Extract（Ω·m）≥ |
80 |
80 |
100 |
100 |
Mass Fraction of Soluble Substance％≤ |
0.5 |
0.5 |
0.5 |
0.5 |
| Speciality | ZA-100 | ZR-940 ZR-940+ |
ZR-948 | ZR-960 | ZR-969 | ZR-110 |
|
98 | 92 | 93 | 92 | 93 | 98 |
| Tint Reducing Power,% | 100 | 100 | 100 | 100 | 100 | 100 |
| Volatile at 105C, %（m/m）<= | 0.5 | 0.8 | 0.5 | 0.5 | 0.5 | 0.5 |
| Mesh Residue(45um), %（m/m）<= | 0.1 | 0.05 | 0.05 | 0.05 | 0.05 | 0.05 |
| pH Value | 6.5-8.0 | 6.5-8.0 | 6.5-7.5 | 6.5-8.0 | 6.5-8.0 | 6.5-8.0 |
| Oil Absorption,g/100g <= | 23 | 23 | 22 | 22 | 20 | 23 |
| Inorganic Treated | —— | Al2O3, SiO2 |
Al2O3 | Al2O3 | Zro2, Al2O3 |
—— |
| Organic Treated | No | Yes | Yes | Yes | Yes | No |
| Proportion(g/cm3): | 3.9 | 4.1 | 4.1 | 4.1 | 4.1 | 4.1 |
| Standard | ||||||
| ISO 591 | A1 | SiO2R2 | R2 | R2 | R2 | R1 |
| ASTM D476 | I | II，III， IV |
II，III | IV | IV | II |
| Types | Coating | Inks | Plastic | Paper | ceramic | Rubber | Others (cosmetic、 cement、wax) |
|||
| indoor | outdoor | power | Profiled Plastic | Masterbatch | ||||||
| ZR-940 | √ | √ | √ | √ | √ | ○ | √ | √ | √ | -- |
| ZR-940 | ☆ | ☆ | ☆ | √ | ☆ | ○ | -- | -- | -- | -- |
| ZR-948 | ☆ | √ | ☆ | ☆ | -- | -- | -- | -- | -- | -- |
| ZR-960 | ○ | ○ | √ | ○ | ☆ | ○ | -- | -- | √ | -- |
| ZR-969 | √ | ☆ | ☆ | √ | ☆ | ○ | -- | ○ | √ | -- |
| ZR-110 | ○ | ○ | ○ | ○ | ○ | ○ | ○ | ○ | ○ | ○ |
| ZR-100 | √ | ○ | ○ | √ | ○ | ○ | √ | ○ | √ | ○ |
Content